Nanosized MnO₂ power has been synthesised at low temperature (160⁰C) by the combustion of gel prepared from  polyvinyl alcohol (PVA) and manganese nitrates. MnO₂ characterization is examined by X-ray diffraction (XRD), scanning electron microscopy (SEM) and BET ( Brunaure-Emmet-Teller) measurements. Further thermal treatment at 160⁰C in 2h yields the single phase MnO₂ with average primary size < 50 nm. It specific surface area is 49 m²/g for MnO₂.